Highly c-axis oriented ZnO:Ni thin film nanostructure by RF magnetron sputtering: Structural, morphological and magnetic studies

Abstract

Nickel doped zinc oxide (ZnO:Ni) thin films with different Ni concentrations were deposited on silicon substrates at 400 °C by reactive magnetron sputtering using a mixture of Ar and O2 gases. The X-ray diffraction and azimuthal patterns of the ZnO:Ni were carried out, and the quality of the strong preferred orientation of crystalline columns in the direction [0 0 1] perpendicular to the substrate surface were analysed. The grain size, distribution, and homogeneity of the thin film surfaces were studied by FE-SEM. The EDX and mapping confirmed that the Ni is incorporated into ZnO uniformly. The microstructure of the textured columns was analysed by TEM and HRTEM analyses. The average thickness and length of the columns were found to be about 50 nm and 600 nm, respectively. The rise of ferromagnetism by the influence of Ni content was studied by VSM magnetic studies at room temperature.