Properties of 34CrMo4 steel before and after cyclic loading

Show simple item record
dc.contributor.advisorMazancová, Eva
dc.contributor.authorHe, Beini
dc.contributor.refereeKučera, Pavel
dc.date.accepted2017-05-29
dc.date.accessioned2017-08-23T09:31:33Z
dc.date.available2017-08-23T09:31:33Z
dc.date.issued2017
dc.description.abstractThis presented diploma work describes the characteristics of 34CrMo4 material, and the properties and microstructures before and after cyclic loading. The obtained results from mechanical properties revealed an increasing of strength of the tested material after cyclic loading. Detected fracture surface showed typical quasi-cleavage fracture. Directly under surface of material the structure was ferritic, and that was changed to ferritic-pearlitic, and then went over to martensite structure. The decarburization and segregation were also observed under the surface.en
dc.description.abstractPrezentovaná diplomová práce popisuje charakteristiky materiálu 34CrMo4, jeho vlastnosti a mikrostruktury před a po cyklickém zatěžování. Získané výsledky mechanických vlastností odhalily po cyklickém zatěžování zvýšení pevnosti testovaného materiálu. Detekovaná lomová plocha vykazovala typické kvazi- štěpné porušení. Přímo pod povrchem materiálu byla struktura feritická, ta se měnila na feriticko-perlitickou a pak přešla do martensitické struktury. Pod povrchem bylo pozorováno oduhličení a segregační pásy.cs
dc.description.department636 - Katedra materiálového inženýrství
dc.description.resultvelmi dobřecs
dc.format.extent8682092 bytes
dc.format.mimetypeapplication/pdf
dc.identifier.otherOSD002
dc.identifier.senderS2736cs
dc.identifier.thesisHEB0012_FMMI_N3923_3911T036_2017
dc.identifier.urihttp://hdl.handle.net/10084/119363
dc.language.isoen
dc.publisherVysoká škola báňská - Technická univerzita Ostravacs
dc.rights.accessopenAccess
dc.subject34CrMo4 steelen
dc.subjectcyclic loadingen
dc.subjectmechanical propertiesen
dc.subjectmicrostructureen
dc.subjectOcel 34CrMo4cs
dc.subjectcyklické zatěžovánícs
dc.subjectmechanické vlastnostics
dc.subjectmikrostrukturacs
dc.thesis.degree-branchProgresivní technické materiálycs
dc.thesis.degree-grantorVysoká škola báňská - Technická univerzita Ostrava. Fakulta metalurgie a materiálového inženýrstvícs
dc.thesis.degree-levelMagisterský studijní programcs
dc.thesis.degree-nameIng.
dc.thesis.degree-programMateriálové inženýrstvícs
dc.titleProperties of 34CrMo4 steel before and after cyclic loadingen
dc.title.alternativeVlastnosti oceli 34CrMo4 před a po cyklickém zatíženícs
dc.typeDiplomová prácecs

Files

Original bundle

Now showing 1 - 3 out of 3 results
Thumbnail Image
Name:
HEB0012_FMMI_N3923_3911T036_2017.pdf
Size:
8.28 MB
Format:
Adobe Portable Document Format
Download
Thumbnail Image
Name:
HEB0012_FMMI_N3923_3911T036_2017_posudek_vedouci_Mazancova_Eva.pdf
Size:
160.97 KB
Format:
Adobe Portable Document Format
Description:
Posudek vedoucího – Mazancová, Eva
Download
Thumbnail Image
Name:
HEB0012_FMMI_N3923_3911T036_2017_posudek_oponent_Kucera_Pavel.pdf
Size:
40.84 KB
Format:
Adobe Portable Document Format
Description:
Posudek oponenta – Kučera, Pavel
Download

Collections

Vysokoškolské kvalifikační práce Fakulty materiálově-technologické / Theses and dissertations of Faculty of Materials Science and Technology (FMT)